{"product_id":"raise3d-hyper-core-ppa-cf25-filament-rfid","title":"Raise3D Hyper Core PPA CF25 Filament - RFID","description":"\u003ch3\u003eRaise3D Hyper Core PPA CF25 Filament - RFID\u003c\/h3\u003e\n\u003cp\u003eColor: Black (RAL 9011)\u003c\/p\u003e\n\u003cp\u003eSpecifications: 1.75 mm\/ 1 kg\u003c\/p\u003e\n\u003cp\u003eThe Hyper Core filament line is oriented towards a new-generation of professional and industrial fiber-reinforced composite filaments for Hyper FFF\u003cstrong\u003e\u003csup\u003e®\u003c\/sup\u003e\u003c\/strong\u003e.\u003c\/p\u003e\n\u003cp\u003eFiber-reinforced composite filaments are the ideal material for industrial and end-use parts production and heavy-duty applications with superio strength, stiff and heat resistance. However, high-speed printing using fiber-reinforced filament brings many challenges, such as lower flowability and poorer interlayer bonding quality, and quicker wearing out of the nozzle.\u003c\/p\u003e\n\u003cp\u003eTo overcome these challenges, Raise3D Hyper Core PPA CF25 filament is an extrusion technology that has been specially developed to form a fiber-rich inner core where most of the carbon fiber (25 wt.%) is well-aligned and distributed. During high-speed printing, the outstanding heat conductivity of the carbon-fiber rich core will speed up filament melting in the hot end. Meanwhile, more residual thermal energy is obtained from the fiber-rich inner core, improving polymer healing and welding processes across the interface of adjacent and lines. Compared to the regular PPA CF, the Hyper Core PPA CF25 significantly improves the Z-direction strength, the surface quality and also the nozzle lifetime. It is ideal for industrial grade applications where high performance, stability and efficiency are required.\u003c\/p\u003e\n\u003cp\u003e\u003cstrong\u003eAbout the RFID version filament\u003c\/strong\u003e\u003c\/p\u003e\n\u003cp\u003eThis version comes with an RFID tag. When printed on the Pro3 HS Series 3D printers, the Pro3 HS Series RFID filament sensor can identify the filament type and verify the print parameters. However, this type of RFID-enabled filament can also be used on other compatible Raise3D 3D printers, even if the printer is not equipped with an RFID sensor.\u003c\/p\u003e\n\u003cp\u003e\u003cstrong\u003ePrinter Compatibility:\u003c\/strong\u003e\u003c\/p\u003e\n\u003cp\u003e\u003ca href=\"https:\/\/3dprintersdepot.com\/products\/raise3d-pro3-large-format-professional-dual-extruder-3d-printer\" target=\"_blank\"\u003eRaise3D Pro3 Series\u003c\/a\u003e with \u003ca href=\"https:\/\/3dprintersdepot.com\/products\/raise3d-hyper-speed-upgrade-kit-pro3-series-only\" target=\"_blank\"\u003eHyper Speed Upgrade Kit\u003c\/a\u003e\u003c\/p\u003e\n\u003cp\u003e\u003ca href=\"https:\/\/3dprintersdepot.com\/products\/raise3d-rmf500-large-volume-industrial-grade-3d-printer\" target=\"_blank\"\u003eRaise3D RMF500\u003c\/a\u003e\u003c\/p\u003e\n\u003cp\u003eFilament Support: \u003ca href=\"https:\/\/3dprintersdepot.com\/products\/raise3d-industrial-ppa-support-filament?_pos=1\u0026amp;_sid=bf70ef252\u0026amp;_ss=r\" target=\"_blank\"\u003eRaise3D Industrial PPA Support\u003c\/a\u003e\u003c\/p\u003e\n\u003cp\u003eNozzle: 0.4 mm (default), 0.2\/ 0.6\/ 0.8\/ 1.0 mm\u003c\/p\u003e\n\u003cp\u003e*Please use the latest ideaMaker Version for Hyper Core PPA CF25 filament.\u003c\/p\u003e\n\u003cp\u003e\u003ca href=\"https:\/\/cdn.shopify.com\/s\/files\/1\/0022\/2671\/6784\/files\/Raise3D_Hyper-Core-PPA-CF25_SDS_US_V1.0_99804dd2-3f01-47fb-9c5d-2a319cc163cc.pdf?v=1783550848\" target=\"_blank\" rel=\"noopener\"\u003eSafety Data Sheet\u003c\/a\u003e\u003c\/p\u003e\n\u003ch3\u003eSpecifications:\u003c\/h3\u003e\n\u003ctable data-sheets-baot=\"1\" data-sheets-root=\"1\" border=\"1\" dir=\"ltr\" cellpadding=\"0\" cellspacing=\"0\" xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd colspan=\"3\" rowspan=\"1\"\u003eGeneral Properties\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eDensity (g\/cm³)\u003c\/td\u003e\n\u003ctd\u003eISO 1183, GB\/T 1033\u003c\/td\u003e\n\u003ctd\u003e1.23\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eWater absorption (%)\u003c\/td\u003e\n\u003ctd\u003eISO 62: Method 1\u003c\/td\u003e\n\u003ctd\u003e1.09\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eDiameter (mm)\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003e1.75\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eNet weight (kg)\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003e1\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eColor\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003eBlack\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eOdor\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003eAlmost odorless\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eSolubility\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003e\n\u003cdiv\u003e\n\u003cdiv\u003eInsoluble in water\u003c\/div\u003e\n\u003c\/div\u003e\n\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003e \u003c\/p\u003e\n\u003ctable style=\"width: 100%;\" data-sheets-baot=\"1\" data-sheets-root=\"1\" border=\"1\" dir=\"ltr\" cellpadding=\"0\" cellspacing=\"0\" xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\"\u003e\n\u003ccolgroup\u003e\n\u003ccol style=\"width: 38.9228%;\" width=\"100\"\u003e\n\u003ccol style=\"width: 27.7439%;\" width=\"100\"\u003e\n\u003ccol style=\"width: 33.3333%;\" width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd colspan=\"3\" rowspan=\"1\"\u003eMechanical Properties (Conditioned, after annealed)\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003e\n\u003cdiv\u003e\n\u003cdiv\u003eTypical Value (XY, Flat)\u003c\/div\u003e\n\u003c\/div\u003e\n\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eYoung’s modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e9989 ±228\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eTensile strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e118 ±4\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eElongation at break (%)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e1.62 ±0.12\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e9214 ±250\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e184 ±6\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eCharpy impact strength (kJ\/m2\u003cbr\u003e)\u003c\/td\u003e\n\u003ctd\u003eISO 179\u003c\/td\u003e\n\u003ctd\u003e7.29 ±0.76\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003eAll testing specimens were printed under the following conditions:\u003cbr\u003eNozzle temp. = 320 ºC; Bed temp.= 80 ºC; Print speed= 45 mm\/s; Infill= 100%; Infill angle= ±45 °.\u003cbr\u003eAll specimens were annealed at 100 ºC for 8h.\u003c\/p\u003e\n\u003ctable xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\" cellspacing=\"0\" cellpadding=\"0\" dir=\"ltr\" border=\"1\" data-sheets-root=\"1\" data-sheets-baot=\"1\" style=\"width: 100%;\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\" style=\"width: 25.0896%;\"\u003e\n\u003ccol width=\"100\" style=\"width: 25.0896%;\"\u003e\n\u003ccol width=\"100\" style=\"width: 25.0896%;\"\u003e\n\u003ccol width=\"100\" style=\"width: 24.7312%;\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"1\" colspan=\"4\"\u003eMechanical Properties (Conditioned, before annealed)\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003cbr\u003e(XY, Flat)\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003cbr\u003e(ZX, Upright)\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eYoung’s modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e8896 ±232\u003c\/td\u003e\n\u003ctd\u003e4214 ±97\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eTensile strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e110 ±2\u003c\/td\u003e\n\u003ctd\u003e58 ±2\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eElongation at break (%)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e2.18 ±0.14\u003c\/td\u003e\n\u003ctd\u003e1.64 ±0.10\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e8487 ±246\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e176 ±4\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eCharpy impact strength (kJ\/m²)\u003c\/td\u003e\n\u003ctd\u003eISO 179\u003c\/td\u003e\n\u003ctd\u003e12.04 ±0.94\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003eAll testing specimens were printed under the following conditions:\u003cbr\u003eNozzle temp.= 320 ºC; Bed temp.= 80 ºC; Print speed= 45 mm\/s; Infill= 100 %; Infill angle= ±45 °.\u003c\/p\u003e\n\u003ctable xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\" cellspacing=\"0\" cellpadding=\"0\" dir=\"ltr\" border=\"1\" data-sheets-root=\"1\" data-sheets-baot=\"1\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"1\" colspan=\"3\"\u003eThermal Properties\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eMelt flow index (g\/10 min)\u003c\/td\u003e\n\u003ctd\u003e300 °C, 2.16 kg\u003c\/td\u003e\n\u003ctd\u003e4.2\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"2\" colspan=\"1\"\u003e\n\u003cdiv\u003eHeat distortion temperature3 \u003cbr\u003e(°C)\u003c\/div\u003e\n\u003c\/td\u003e\n\u003ctd\u003eISO 75 @0.45 MPa\u003c\/td\u003e\n\u003ctd\u003e197\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eISO 75 @1.8 MPa\u003c\/td\u003e\n\u003ctd\u003e124\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003eThe specimens of HDT test were annealed at 100 ºC for 8h.\u003cbr\u003e\u003c\/p\u003e\n\u003ctable xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\" cellspacing=\"0\" cellpadding=\"0\" dir=\"ltr\" border=\"1\" data-sheets-root=\"1\" data-sheets-baot=\"1\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"1\" colspan=\"2\"\u003eOther Information\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eColor\u003c\/td\u003e\n\u003ctd\u003eColor Code\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBlack\u003c\/td\u003e\n\u003ctd\u003eRAL 7024\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003e \u003c\/p\u003e\n\u003ch2\u003eSpecifications:\u003c\/h2\u003e\n\u003ctable data-sheets-baot=\"1\" data-sheets-root=\"1\" border=\"1\" dir=\"ltr\" cellpadding=\"0\" cellspacing=\"0\" xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd colspan=\"3\" rowspan=\"1\"\u003eGeneral Properties\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eDensity (g\/cm³)\u003c\/td\u003e\n\u003ctd\u003eISO 1183, GB\/T 1033\u003c\/td\u003e\n\u003ctd\u003e1.23\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eWater absorption (%)\u003c\/td\u003e\n\u003ctd\u003eISO 62: Method 1\u003c\/td\u003e\n\u003ctd\u003e1.09\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eDiameter (mm)\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003e1.75\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eNet weight (kg)\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003e1\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eColor\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003eBlack\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eOdor\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003eAlmost odorless\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eSolubility\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003ctd\u003e\n\u003cdiv\u003e\n\u003cdiv\u003eInsoluble in water\u003c\/div\u003e\n\u003c\/div\u003e\n\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003e \u003c\/p\u003e\n\u003ctable style=\"width: 100%;\" data-sheets-baot=\"1\" data-sheets-root=\"1\" border=\"1\" dir=\"ltr\" cellpadding=\"0\" cellspacing=\"0\" xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\"\u003e\n\u003ccolgroup\u003e\n\u003ccol style=\"width: 38.9228%;\" width=\"100\"\u003e\n\u003ccol style=\"width: 27.7439%;\" width=\"100\"\u003e\n\u003ccol style=\"width: 33.3333%;\" width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd colspan=\"3\" rowspan=\"1\"\u003eMechanical Properties (Conditioned, after annealed)\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003e\n\u003cdiv\u003e\n\u003cdiv\u003eTypical Value (XY, Flat)\u003c\/div\u003e\n\u003c\/div\u003e\n\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eYoung’s modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e9989 ±228\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eTensile strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e118 ±4\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eElongation at break (%)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e1.62 ±0.12\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e9214 ±250\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e184 ±6\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eCharpy impact strength (kJ\/m2\u003cbr\u003e)\u003c\/td\u003e\n\u003ctd\u003eISO 179\u003c\/td\u003e\n\u003ctd\u003e7.29 ±0.76\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003eAll testing specimens were printed under the following conditions:\u003cbr\u003eNozzle temp. = 320 ºC; Bed temp.= 80 ºC; Print speed= 45 mm\/s; Infill= 100%; Infill angle= ±45 °.\u003cbr\u003eAll specimens were annealed at 100 ºC for 8h.\u003c\/p\u003e\n\u003ctable xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\" cellspacing=\"0\" cellpadding=\"0\" dir=\"ltr\" border=\"1\" data-sheets-root=\"1\" data-sheets-baot=\"1\" style=\"width: 100%;\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\" style=\"width: 25.0896%;\"\u003e\n\u003ccol width=\"100\" style=\"width: 25.0896%;\"\u003e\n\u003ccol width=\"100\" style=\"width: 25.0896%;\"\u003e\n\u003ccol width=\"100\" style=\"width: 24.7312%;\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"1\" colspan=\"4\"\u003eMechanical Properties (Conditioned, before annealed)\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003cbr\u003e(XY, Flat)\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003cbr\u003e(ZX, Upright)\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eYoung’s modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e8896 ±232\u003c\/td\u003e\n\u003ctd\u003e4214 ±97\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eTensile strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e110 ±2\u003c\/td\u003e\n\u003ctd\u003e58 ±2\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eElongation at break (%)\u003c\/td\u003e\n\u003ctd\u003eISO 527\u003c\/td\u003e\n\u003ctd\u003e2.18 ±0.14\u003c\/td\u003e\n\u003ctd\u003e1.64 ±0.10\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending modulus (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e8487 ±246\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBending strength (MPa)\u003c\/td\u003e\n\u003ctd\u003eISO 178\u003c\/td\u003e\n\u003ctd\u003e176 ±4\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eCharpy impact strength (kJ\/m²)\u003c\/td\u003e\n\u003ctd\u003eISO 179\u003c\/td\u003e\n\u003ctd\u003e12.04 ±0.94\u003c\/td\u003e\n\u003ctd\u003e\/\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003eAll testing specimens were printed under the following conditions:\u003cbr\u003eNozzle temp.= 320 ºC; Bed temp.= 80 ºC; Print speed= 45 mm\/s; Infill= 100 %; Infill angle= ±45 °.\u003c\/p\u003e\n\u003ctable xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\" cellspacing=\"0\" cellpadding=\"0\" dir=\"ltr\" border=\"1\" data-sheets-root=\"1\" data-sheets-baot=\"1\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"1\" colspan=\"3\"\u003eThermal Properties\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eProperty\u003c\/td\u003e\n\u003ctd\u003eTesting Method\u003c\/td\u003e\n\u003ctd\u003eTypical Value\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eMelt flow index (g\/10 min)\u003c\/td\u003e\n\u003ctd\u003e300 °C, 2.16 kg\u003c\/td\u003e\n\u003ctd\u003e4.2\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"2\" colspan=\"1\"\u003e\n\u003cdiv\u003eHeat distortion temperature3 \u003cbr\u003e(°C)\u003c\/div\u003e\n\u003c\/td\u003e\n\u003ctd\u003eISO 75 @0.45 MPa\u003c\/td\u003e\n\u003ctd\u003e197\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eISO 75 @1.8 MPa\u003c\/td\u003e\n\u003ctd\u003e124\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003eThe specimens of HDT test were annealed at 100 ºC for 8h.\u003cbr\u003e\u003c\/p\u003e\n\u003ctable xmlns=\"http:\/\/www.w3.org\/1999\/xhtml\" cellspacing=\"0\" cellpadding=\"0\" dir=\"ltr\" border=\"1\" data-sheets-root=\"1\" data-sheets-baot=\"1\"\u003e\n\u003ccolgroup\u003e\n\u003ccol width=\"100\"\u003e\n\u003ccol width=\"100\"\u003e\n\u003c\/colgroup\u003e\n\u003ctbody\u003e\n\u003ctr\u003e\n\u003ctd rowspan=\"1\" colspan=\"2\"\u003eOther Information\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eColor\u003c\/td\u003e\n\u003ctd\u003eColor Code\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003ctr\u003e\n\u003ctd\u003eBlack\u003c\/td\u003e\n\u003ctd\u003eRAL 7024\u003c\/td\u003e\n\u003c\/tr\u003e\n\u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003e \u003c\/p\u003e","brand":"Raise3D","offers":[{"title":"Default Title","offer_id":42014464671826,"sku":null,"price":233.95,"currency_code":"EUR","in_stock":true}],"thumbnail_url":"\/\/cdn.shopify.com\/s\/files\/1\/0022\/2671\/6784\/files\/Raise3D-Hyper-Core-PPA-CF25_Black_01.jpg?v=1743709174","url":"https:\/\/3dprintersdepot.com\/en-fr\/products\/raise3d-hyper-core-ppa-cf25-filament-rfid","provider":"3D Printers Depot®","version":"1.0","type":"link"}